Board pieces, flexible wiring boards, and processes for manufacturing flexible wiring boards

ABSTRACT

A board piece  2  of the present invention comprises a non-thermoplastic resin film  11 , a thermoplastic resin film  10  formed on the non-thermoplastic resin film  11  and a metal wiring  8  formed on the surface of the thermoplastic resin film  10 . Metal wiring  8  is partially exposed on board piece  2  to form a contact  12 . A low-melting metal coating  13  is formed on contact  12  and two board pieces  2   a   , 2   b  are pressed against each other under heating with contacts  12   a   , 12   b  thereof being in contact with each other so that thermoplastic resin films  10   a   , 10   b  soften to adhere board pieces  2   a   , 2   b  to each other and low-melting metal coatings  13   a   , 13   b  melt and then solidify to connect contacts  12   a   , 12   b  to each other. The region of metal wiring  8  not used for connection is wiring  17  connecting contacts  12  to each other and a cover film  19  can be provided on the surface thereof. Contacts  12   a   , 12   b  can also be connected by applying ultrasonic wave.

FIELD OF THE INVENTION

The present invention relates to the field of flexible wiring boards, particularly to the field of board pieces constituting flexible wiring boards and flexible wiring boards formed by assembling the board pieces.

PRIOR ART

Flexible wiring boards having a desired circuit pattern printed thereon have been widely used, and in recent years, there are demands for flexible wiring boards having various shapes suitable for the contours of the place where they are used.

FIG. 10(a) shows a layout for cutting T-shaped flexible wiring boards 252 from a rectangular pre-cutted substrate 250, in which six flexible wiring boards 252 are obtained.

However, a significant part of pre-cutted substrate 250 is uselessly discarded when such shaped flexible wiring boards 252 are cut.

Thus, a technique for preparing a flexible wiring board in a complex shape was proposed by dissolving the complex shape into simple shapes and assembling board pieces in the A simple shapes. Reference 255 in FIG. 10(c) represents a flexible wiring board having the same shape as that of flexible wiring board 252 described above and formed by assembling two rectangular board pieces 253, 254.

When rectangular board pieces 253, 254 are used in this manner, a close layout can be achieved as shown in FIG. 10(b) and therefore, precut substrate 250 can be effectively used by cutting board pieces 253, 254 in simple shapes. In FIG. 10(b), eight board pieces each 253, 254 are obtained and assembled into eight flexible wiring boards 255. As shown in this example, a greater number of flexible wiring boards 255 can be obtained by using board pieces in simple shapes than directly cutting T-shaped flexible wiring boards 252.

When a plurality of board pieces are assembled into a flexible wiring board as described above, board pieces 253, 254 must be mechanically and electrically assembled.

An example of the assembling technique is explained with reference to FIGS. 11(a), 11(b), in which references 220, 230 represent board pieces having metal wirings 222, 232 consisting of a patterned copper thin film formed on polyimide films 221, 231, respectively. In order to assemble these board pieces 220, 230, boards elements 220, 230 are first opposed to each other with metal wirings 222, 232 facing each other.

Metal wirings 222, 232 have solder coatings 223, 233 formed by plating on their surfaces, respectively, and solder coatings 223, 233 of the respective board pieces 220, 230 are brought into close contact with each other and heat and pressure are applied to melt solder coatings 223, 233, which are then cooled to form a solder layer 204. This solder layer 204 forms a metallic bond with metal wirings 222, 232, whereby metal wirings 222, 232 are firmly connected to each other via solder layer 204 to give a flexible wiring board 203 (FIG. 11(b)).

However, the recent need for forming a large number of metal wirings on a small-area flexible wiring board leads to an increasingly narrower pitch between metal wirings 222 (or metal wirings 232) on the same board piece 220, 230.

When solder coatings 223, 233 are heated under pressure as described above, molten solder scatters and remains here and there as scatter 215 in flexible wiring board 203, and in extreme cases, molten solder flows out to form a bridge 216 at connection 212 between metal wirings 222, 232, which causes a short circuit between metal wirings 222 (or metal wirings 232) to be insulated.

As the pitch between metal wirings 222 (or metal wirings 232) becomes narrower, bridge 216 becomes more likely to occur. Especially when a plurality of board pieces are to be assembled into a flexible wiring board, even one short circuit at the connection between board pieces means a faulty flexible wiring board as a whole, which extremely lowers the manufacturing yield of flexible wiring boards.

DISCLOSURE OF THE INVENTION

A board piece of the present invention comprises a non-thermoplastic resin film, a thermoplastic resin film formed on the non-thermoplastic resin film and a metal wiring formed on the surface of the thermoplastic resin film.

In this board piece, the metal wiring can be partially covered with a resin film.

The metal wiring can also be partially exposed.

A low-melting metal coating can be formed on at least a part of the exposed metal wiring.

A solder can be used as a material for the low-melting metal coating.

A gold coating can also be formed on at least a part of the exposed metal wiring.

The non-thermoplastic resin film can consist of a polyimide film.

The thermoplastic resin film can consist of a thermoplastic polyimide film.

A flexible wiring board of the present invention comprises at least two board pieces each having a non-thermoplastic resin film, a thermoplastic resin film formed on the non-thermoplastic film and a metal wiring formed on the surface of the thermoplastic resin film, wherein the board pieces are adhered to each other via the thermoplastic resin films by heating the metal wirings of the board pieces in contact with each other to soften the thermoplastic resin films and insert them between connections of the metal wirings in contact with each other.

In the flexible wiring board, a low-melting metal coating can be formed on the surface of at least one of the metal wirings in contact with each other so that the board pieces are heated to melt the low-melting metal coating, which then solidifies to connect the metal wirings to each other.

The metal wirings in contact with each other can also be connected by ultrasonic wave vibration.

In this case, a gold coating is preferably formed on at least one of the metal wirings to be connected by ultrasonic wave vibration.

Another flexible wiring board of the present invention is formed by assembling at least three board pieces each having a resin film and a metal wiring, wherein the metal wirings of a first and second board pieces among the board pieces are partially connected and fixed to the metal wiring of a third board piece and a thermoplastic resin is filled between the connecting and fixing regions of the metal wirings while the other regions of the metal wirings are partially covered with a protective film on their surfaces and partially exposed.

In the flexible wiring board, the resin film of at least one of the board pieces to be assembled has a multilayer structure consisting of a non-thermoplastic resin film and a thermoplastic resin film and the metal wiring can be formed on the thermoplastic resin film.

The board pieces can be connected to each other by applying a thermoplastic resin film on each of the metal wirings and then assembling the board pieces with a thermoplastic resin constituting the thermoplastic resin film being filled between the connecting regions of the metal wirings.

The metal wirings can be fixed to each other with a solder.

An opening can be formed in the protective film provided on at least one of the first to third board pieces.

In a process for manufacturing a flexible wiring board of the present invention by assembling a plurality of board pieces having a resin film and a metal wiring provided on the resin film, the resin film of at least one of the board pieces to be assembled has a multilayer structure consisting of a non-thermoplastic resin film and a thermoplastic resin film and the metal wiring is provided on the thermoplastic resin film and the board pieces to be assembled are pressed against each other under heating.

In this case, the metal wirings of the board pieces can be connected to each other by forming a low-melting metal coating on the surface of the metal wiring of at least one of the board pieces to be assembled and pressing the board pieces against each other under heating to melt the low-melting metal coating.

The board pieces can be assembled by pressing the board pieces against each other under heating after applying ultrasonic wave to the board pieces in a superposed state to connect the metal wirings of the board pieces to each other by vibration energy of the ultrasonic wave.

The board pieces can also be assembled by pressing the board pieces in a superposed state against each other under heating while applying ultrasonic wave to connect the metal wirings to each other by vibration energy of the ultrasonic wave.

In this case, a gold coating is preferably formed in advance on the surface of at least one of the metal wirings to be connected.

In another process for manufacturing a flexible wiring board of the present invention by assembling a plurality of board pieces having a resin film and a metal wiring provided on the resin film, the metal wirings of the board pieces are connected to each other by providing a thermoplastic resin film between the metal wirings of the board pieces to be assembled and pressing the board pieces against each other under heating to force the metal wirings into the thermoplastic resin film.

In this case, the metal wirings of the board pieces can be connected to each other by forming a low-melting metal coating on the surface of the metal wiring of at least one of the board pieces to be assembled and pressing the board pieces against each other under heating to melt the low-melting metal coating.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1(a)-(h) is a diagram for illustrating a first example of flexible wiring board of the present invention and a manufacturing process thereof.

FIGS. 2(a), (b) is a diagram for illustrating a variation of the first example of flexible wiring board of the present invention and a manufacturing process thereof.

FIG. 3 shows an example of an ultrasonic wave apparatus used in a process of the present invention.

FIGS. 4(a)-(d) is a diagram for illustrating a second example of flexible wiring board of the present invention and a manufacturing process thereof.

FIGS. 5(a)-(d) is a diagram for illustrating a third example of flexible wiring board of the present invention and a manufacturing process thereof.

FIGS. 6(a)-(e) is a diagram for illustrating a fourth example of flexible wiring board of the present invention and a manufacturing process thereof.

FIGS. 7(a)-(d) is a diagram for illustrating a fifth example of flexible wiring board of the present invention and a manufacturing process thereof.

FIGS. 8(a)-(e) is a diagram for illustrating a sixth example of flexible wiring board of the present invention and a manufacturing process thereof.

FIGS. 9(a)-(c) is a diagram for illustrating an example of a layout of board pieces.

FIGS. 10(a)-(c) is a diagram for illustrating a layout of board pieces and flexible wiring boards.

FIGS. 11(a), (b) is a diagram for illustrating disadvantages of an assembling technique of the prior art.

THE MOST PREFERRED EMBODIMENTS OF THE INVENTION

The present invention was made to overcome the above disadvantages of the prior art with the purpose of providing a technique for assembling a plurality of board pieces to give a shaped flexible wiring board with high reliability and high durability.

Board pieces and flexible wiring boards of the present invention will now be explained as well as manufacturing processes of flexible wiring boards with reference to the attached drawings.

FIGS. 1(a)-(h) shows a process for manufacturing a first example of flexible wiring board of the present invention.

Referring to FIGS. 1(a), 1(b), a thermoplastic resin film 10 consisting of a thermoplastic polyimide synthesized from an aliphatic amine and an acid anhydride and a non-thermoplastic resin film 11 consisting of a non-thermoplastic polyimide synthesized from an aromatic amine and an acid anhydride are first prepared.

An adhesive layer (not shown with a release paper applied thereon) is formed on each side of thermoplastic resin film 10 (preferably having a thickness of 15 μm-50 μm and here consisting of a polyimide film having a thickness of 25 μm) and the adhesive layer on one side is exposed, and thermoplastic resin film 10 is applied on non-thermoplastic resin film 11 (preferably having a thickness of 10 μm-50 μm and here consisting of a polyimide film having a thickness of 25 μm available from DuPont under trade name Kapton) (FIG. 1(b)), and then the other adhesive layer is exposed and a metal foil 9 (preferably having a thickness of 5 μm-75 μm and here consisting of a copper foil having a thickness of 18 μm) is applied on the surface of thermoplastic resin film 10 (FIG. 1(c)).

Then, metal foil 9 is patterned by a photolythographic process using a photosensitive dry film or a resist film to form a metal wiring 8 consisting of copper (FIG. 1(d)). Metal wiring 8 typically has a pattern width of about 100 μm with a pitch of about 10 μm-200 μm, here 200 μm (0.2 mm).

This metal wiring 8 has a wide contact for connecting board pieces to each other to form a flexible wiring board or, after a flexible wiring board has been prepared, for connecting the flexible wiring board to an electric component such as a semiconductor device or an electronic circuit. It also has an elongate wiring for electrically connecting contacts via metal wiring 8.

In FIG. 1(e), reference 12 represents the contact and reference 17 represents the wiring. After metal wiring 8 is formed and surface-cleaned, a cover film 19 is applied on wiring 17 while contact 12 is exposed as shown in FIG. 1(e).

The assembly is immersed in a plating solution of a low-melting metal (here, a solder of Sn:Pb =6:4) to form a low-melting metal coating 13 on the top of contact 12, whereby a board piece 2 is obtained (FIG. 1(f)). Preferably, low-melting metal coating 13 has a thickness of 1 μm-10 μm. The thickness here is 3 μm.

Then, two board pieces 2 a, 2 b having the structure described above are prepared and their contacts 12 a, 12 b are opposed (FIG. 1(g)) and heat and pressure are applied while low-melting metal coatings 13 a, 13 b on the tops of contacts 12 a, 12 b are in close contact with each other (thermal compression bonding). As an example, thermal compression bonding conditions involve a heating temperature of 150-300° C. at a pressure of 20-50 kg/cm² for 10-20 seconds, and here 200° C. at 30 kg/cm² for 10 seconds.

During thermal compression bonding of board pieces 2 a, 2 b, thermoplastic resin films 10 a, 10 b and contacts 12 a, 12 b are first heated via non-thermoplastic films 11 a, 11 b and thermoplastic resin films 10 a, 10 b heat up and soften.

Thermoplastic resin films 10 a, 10 b located between contacts 12 a (and between contacts 12 b) are not in contact with each other before heating, but they are flown out and inserted between contacts 12 a (and between contacts 12 b) as they soften.

After thermoplastic resin films 10 a, 10 b soften, the temperature of contacts 12 a, 12 b rises, and when it reaches the melting point of the low-melting metal or more, low-melting metal coatings 13 a, 13 b melt. At that time, melts of low-melting metal coatings 13 a, 13 b cannot scatter or flow out to form a bridge by molten solder because softened thermoplastic resin films 10 a, 10 b are filled between contacts 12 a (and between contacts 12 b) in board pieces 2 a, 2 b of the present invention.

When cooling after thermal compression bonding, two molten low-melting metal coatings 13 a, 13 b combine to form a low-melting metal coating 14. Contacts 12 a, 12 b and low-melting metal coating 14 combine to form connection 16 (FIG. 1(h)).

Copper on the surfaces of contacts 12 a, 12 b forms a metallic bond with low-melting metal coating 14 so that two board pieces 2 a, 2 b are electrically and mechanically connected via connection 16. Around this connection 16 is formed a flange 14′ protruding from low-melting metal coating 14.

When cooling after the end of compression bonding, two softened thermoplastic resin films 10 a, 10 b also combine to form a thermoplastic resin film 15. As thermoplastic resin films 10 a, 10 b develop adhesiveness when then soften, two non-thermoplastic resin films 11 a, 11 b are adhered to each other via single layer thermoplastic resin film 15 to give a first example of flexible wiring board 5 of the present invention. In this flexible wiring board 5, wirings 17 a, 17 b of two board pieces 2 a, 2 b adhered are covered with cover films 19 a, 19 b, respectively.

Although boards elements 2 a, 2 b described above both have contacts 12 a, 12 b formed on thermoplastic resin films 10 a, 10 b, either one board piece may have a contact formed on the thermoplastic resin film.

For example, a flexible wiring board can be prepared by assembling a board piece represented by reference 3 in FIG. 2(a) and a board piece represented by reference 2 in FIG. 1. Board piece 3 in FIG. 2(a) has a contact 32 and a wiring 37 consisting of a metal wiring formed on a non-thermoplastic resin film 31.

Also in this case, low-melting metal coatings 13, 33 on the tops of contacts 12, 32 of two board pieces 2, 3 are first brought into contact with each other and heat and pressure are applied in this state to form a low-melting metal coating 34, whereby the low-melting metal coating 34 and contacts 12, 32 form a connection 36. Board pieces 2, 3 are mechanically and electrically connected via connection 36 to give a flexible wiring board represented by reference 7 in FIG. 2(b).

The low-melting metal neither scatters nor forms a bridge because low-melting metal coatings 13, 33 melt after thermoplastic resin film 10 of one board piece 2 softens to fill the gap between contacts 32 directly formed on non-thermoplastic resin film 31 of the other board piece 3.

Although each of board pieces 2 (2 a, 2 b) and 3 used for assembly described above and board pieces described below has metal wiring 8 formed on one side, a metal wiring may be formed on each side.

Although non-thermoplastic resin films 11 (11 a, 11 b), 31 and thermoplastic resin film 10 (10 a, 10 b) described above are polyimide resin films, the present invention is not limited thereto. In the case of board pieces 2 (2 a, 2 b) and 3 described above and board pieces described below, thermoplastic resin films that cannot dissolve during thermal compression bonding but develop adhesiveness as they soften can be used. Resins for thermoplastic resin films are desirably polyimide resins from the viewpoint of chemical resistance and flame retardance.

When metal wirings are to be connected via a low-melting coating, the softening point of each of thermoplastic resin films 11 (11 a, 11 b) and 31 described above and thermoplastic resin films described below must be lower than the melting temperature of low-melting metal coatings 13, 33, but common thermoplastic resin films satisfy this condition.

Suitable low-melting metals for use in the present invention other than solders include tin series metals, bismuth series metals, etc. A corrosion resistant metal coating such as an oxidation resistant and corrosion resistant gold coating may be formed on the surfaces of low-melting metal coatings of the embodiments described above and below.

According to the present invention, the non-thermoplastic resin film of one of board pieces to be assembled and the non-thermoplastic resin film of the other board piece are adhered to each other via a thermoplastic resin film.

Therefore, a flexible wiring board of the present invention can also be formed by providing a contact on the surface of each metal wiring without forming a low-melting metal coating and applying heat and pressure while the contacts of board pieces are in contact, whereby the contacts are bonded to electrically connect metal wirings.

Metal wirings can also be ultrasonically connected.

Reference 60 in FIG. 3 represents an ultrasonic wave apparatus used for ultrasonic wave connection. This ultrasonic wave apparatus 60 comprises a cylindrical ultrasonic wave generator 61, a resonator 62 transmitting ultrasonic wave vibration to an object, a platform 66 and two guides 67 ₁, 67 ₂.

In this ultrasonic wave apparatus 60, guides 67 ₁, 67 ₂ are upright almost perpendicularly on platform 66 and ultrasonic wave generator 61 is fitted to guide 67 ₁, 67 ₂ in a horizontal position to be vertically movable. Ultrasonic wave generator 61 is designed to rest at a desired position on guide 67 ₁, 67 ₂.

The base of resonator 62 is fitted to the tip end of ultrasonic wave generator 61. The tip end of resonator 62 is bent so that its surface is horizontal. Reference 69 represents such a horizontal surface of the tip end of resonator 62. Reference 81 represents the central axis of ultrasonic wave generator 61 and resonator 62, and the central axis 81 is designed to be horizontal together with the surface 69 of the tip end.

References 4 a, 4 b in FIGS. 4(a)-(d) represent board pieces to be worked by the ultrasonic wave apparatus 60. These board pieces 4 a, 4 b have the same structure as that of board piece 2 shown in FIG. 1(e) except that low-melting metal coatings 13 a, 13 b are replaced with gold coatings 23 a, 23 b, and similar members are designated by similar references and not explained. A process for manufacturing a second example of flexible wiring board of the present invention using these board pieces 4 a, 4 b is explained below.

A workbench 68 having a flat upper surface is provided on platform 66 and two board pieces 4 a, 4 b are mounted on workbench 68 with gold coatings 23 a, 23 b formed on their contacts 12 a, 12 bbeing in contact with each other.

Then, an air cylinder 63 located above resonator 62 is activated so that ultrasonic wave generator 61 and resonator 62 vertically descend along guides 67 ₁, 67 ₂ until the surface 69 of the tip end of resonator 62 comes into contact with non-thermoplastic resin film 11 b of board piece 4 b.

This state is shown in FIG. 4(a), and when ultrasonic wave generator 61 is activated, ultrasonic wave vibration generated from the ultrasonic wave generator 61 is transmitted to board pieces 4 a, 4 b via resonator 62.

The direction of ultrasonic wave vibration generated in ultrasonic wave generator 61 has almost no components vertical to the surface 69 of the tip end of ultrasonic wave generator 61 but consists of only components parallel to central axis 81 of ultrasonic wave generator 61.

As ultrasonic wave generator 61 is horizontally oriented, ultrasonic wave vibration is applied in the direction horizontal to the surfaces of board pieces 4 a, 4 b.

During then, board piece 4 a directly mounted on workbench 68 remains fixed by frictional force against the surface of workbench 68. Thus, gold coatings 23 a, 23 b are slid on each other under ultrasonic wave vibration so that they are joined. This state is shown in FIG. 4(b), in which two gold coatings 23 a, 23 b are joined to form a single layer gold coating 24.

Reference 26 represents a connection for electrically connecting board pieces 4 a, 4 b. This connection 26 consists of gold coating 24 formed by ultrasonic wave connection and contacts 12 a, 12 b.

Then, ultrasonic wave generator 61 is stopped and then air cylinder 63 is activated so that resonator 62 and ultrasonic wave generator 61 ascend along guides 67 ₁, 67 ₂ to remove connected board pieces 4 a, 4 b from the top of workbench 68.

Then, board pieces 4 a, 4 b are mounted on another workbench 28 and a heat-generating member 29 is pressed against the part including gold coating 24 to heat thermoplastic resin films 10 a, 10 b, whereby thermoplastic resin films 10 a, 10 b heat up and soften and after cooling, a thermoplastic resin film 15 is formed. Thermoplastic resin films 10 a, 10 b enter into connection 26 when they are heated. Board pieces 4 a, 4 b are connected to each other via the resulting thermoplastic resin film 15 to give a second example of flexible wiring board 6 of the present invention (FIG. 4(c)).

If resonator 62 can be made to generate heat, resonator 64 is heated to a specific temperature and brought into contact with board pieces 4 a, 4 b superposed as shown in FIG. 4(a) and ultrasonic wave is applied under pressure so that ultrasonic wave is first applied between two metal coatings 23 a, 23 b to connect contacts 12 a, 12 b of board pieces 4 a, 4 b via metal coating 24 obtained by ultrasonic wave connection.

When ultrasonic wave application is terminated while resonator 62 remains in a pressed state, thermoplastic resin films 10 a, 10 b soften to give a second example of flexible wiring board 6 of the present invention in the same way as described above as shown in FIG. 4(d). In this case, board pieces 4 a, 4 b can be assembled via thermoplastic resin films 10 a, 10 b without moving them from the top of workbench 68 of ultrasonic wave apparatus 60.

Although this second example of flexible wiring board 6 uses board pieces 4 a, 4 b having gold coatings 23 a, 23 b, gold coatings may be replaced with another low-melting coatings based on gold and further containing other metals. Platinum, silver and palladium coatings as well as another low-melting coatings based on these metals CL and further containing other metals may also be used.

Instead of using gold coatings or platinum coatings, board pieces 2 a, 2 b, 3 having low-melting metal coatings 13 a, 13 b, 33 such as board pieces 2 a, 2 b shown in FIG. 1 or board piece 3 shown in FIG. 2 can be used to ultrasonically connect low-melting metal coatings 13 a, 13 b, 33. In this case, a flexible wiring board can be prepared by applying heat and pressure after ultrasonic wave connection or by using a heated resonator for applying ultrasonic wave under heat and pressure. When ultrasonic wave is applied to board pieces 2, 3 shown in FIG. 2 under heat and pressure, the resonator of the ultrasonic wave apparatus should preferably be brought into contact with board piece 3 having a metal wiring (contact 32 and wiring 37) formed on non-thermoplastic resin film 31. When heat is applied after or during ultrasonic wave application, board pieces shown in FIGS. 5-8 can also be used.

Next, other examples of flexible wiring board of the present invention are explained together with manufacturing processes thereof with reference to the attached drawings.

FIG. 9(a) shows a layout for cutting H-shaped flexible wiring boards 192 from a rectangular pre-cutted substrate 190, in which four flexible wiring boards 192 are obtained.

In contrast, three kinds of board pieces 193, 194, 195 can be closely arranged on pre-cutted substrate 190 according to the present invention as shown in FIG. 9(b). A flexible wiring board 196 shown in FIG. 9(c) can be prepared by cutting and assembling these three kinds of board pieces 193, 194, 195. With the layout of board pieces 193, 194, 195 in FIG. 9(b), six flexible wiring boards 196 can be obtained.

A process for assembling at least three board pieces 193, 194, 195 to form a flexible wiring board 192 as described above is explained below.

References 101 a, 101 b, 101 c in FIGS. 5(a)-5(d) represent board pieces corresponding to the board pieces 193, 194, 195, and these board pieces 101 a, 101 b, 101 c are assembled to form a third example of flexible wiring board 105 of the present invention (flexible wiring board represented by reference 105 in FIGS. 5(c), 5(d)) as follows.

Referring to FIG. 5(a), each of board pieces 101 a, 101 b, 101 c has a multilayer resin film consisting of a non-thermoplastic resin film 111 and a thermoplastic resin film 115 formed on the non-thermoplastic resin film 111. On the surface of thermoplastic resin film 115 is formed a patterned metal wiring 161.

Non-thermoplastic resin film 111 consists of a polyimide film synthesized from an aromatic diamine and an acid anhydride, while thermoplastic resin film 115 consists of a polyimide film synthesized from an aliphatic amine and an acid anhydride.

Metal wiring 161 consists of a copper thin film 121 and a low-melting metal coating (solder coating) 125 formed on the copper thin film 121. On the top of metal wiring 125 of each board piece 101 a, 101 b, 101 c, a polyamidic acid film before imidation is first formed and a photoresist is applied all over the surface, and then the photoresist is patterned by exposure and development and the polyamidic acid film is etched according to the pattern of the photoresist and imidated by heat treatment after removal of the photoresist to form a non-thermoplastic protective film 151.

At openings in this protective film 151 is exposed metal wiring 161 as shown by reference 135 as exposed regions. In regions where protective film 151 exists, metal wiring 161 is covered with protective film 151 to form protected regions shown by reference 131.

Referring to FIG. 5(b), two exposed regions 135 of one board piece 101 a among these board pieces 101 a, 101 b, 101 c are opposed to exposed regions 135 of the other two board pieces 101 b, 101 c. Metal wiring 161 of the one board piece 101 a is brought into contact with metal wirings 161 of the other board pieces 101 b, 101 c (low-melting coatings 125 on the surfaces of metal wirings 161 are brought into contact with each other) and heat and pressure are applied so that thermoplastic resin film 115 first softens and thermoplastic resin film 115 below the bottom of pressed metal wiring 161 softens and enters into the gap between metal wirings 161. As a result, the gap between metal wirings 161 is filled with the thermoplastic resin.

As the temperature of metal wirings 161 further rises in this state, low-melting metal coatings 125 on the surfaces of copper thin films 121 melt. However, melts of low-melting metal coatings 125 cannot scatter so that no short circuit occurs between metal wirings 161 because the thermoplastic resin of thermoplastic resin films 115 is filled between metal wirings 161.

Referring to FIG. 5(c), low-melting metal coatings 125 melt and then solidify into one piece when cooled. Reference 119 represents a low-melting metal coating as one piece. Metal wirings 161 are electrically and mechanically connected via the resulting one piece low-melting metal coating 119 to form a connection 141. Non-thermoplastic resin films 111 of board pieces 101 a, 101 b, 101 c opposed to each other are also connected to each other via thermoplastic resin films 115.

Thus, board pieces 101 a, 101 b, 101 c are firmly connected via connections 141 of metal wirings 161 and thermoplastic resin films 115 to give a flexible wiring board 105 (FIG. 5(c)).

FIG. 5(d) shows an end region of board pieces 101 b, 101 c where connection 141 is not formed among exposed regions 135 of board pieces 101 b, 101 c. In this region, metal wiring 161 is exposed and used as an external terminal 145 for connecting flexible wiring board 105 to an outer circuit.

In this flexible wiring board 105, protective film 151 is provided on metal wiring 161 except for connection 141 or external terminal 145 to form protected region 131.

Next, a fourth example of flexible wiring board of the present invention is explained.

Referring to FIG. 6(a), reference 102 a, 102 b, 102 c represent board pieces used for preparing a fourth example of flexible wiring board 106 of the present invention (flexible wiring board represented by reference 106 in FIGS. 6(d), (e)).

This board piece 102 a, 102 b, 102 c has a multilayer resin film consisting of a non-thermoplastic resin film 112 and a thermoplastic resin film 116 formed on the surface thereof. On the top of the thermoplastic resin film 116 is formed a patterned metal wiring 162. Metal wiring 162 consists of a copper thin film 122 and a low-melting metal coating 126 formed on the surface thereof.

Unlike board pieces 101 a, 101 b, 101 c of the above third example, each board piece 102 a, 102 b, 102 c has no protective film on metal wiring 162.

Referring to FIG. 6(b), some of exposed regions 136 of metal wiring 162 of one board piece 102 a among board pieces 102 a, 102 b, 102 c is opposed to exposed regions 136 of the other two board pieces 102 b, 102 c.

Metal wirings 162 in the exposed regions 136 are brought into contact with each other and heat and pressure are applied so that thermoplastic resin films 116 first soften and flow out from bottom of pressed metal wirings 162 and the gap between metal wirings 162 is filled with the thermoplastic resin. Then, low-melting metal coatings 126 melt without scattering, and board pieces 102 a, 102 b; 102 c are cooled to form a connection 142 at which metal wirings 162 are connected and fixed to each other. This state is shown in FIG. 6(c). In this figure, reference 129 represents a low-melting metal coating formed by melting and solidifying two low-melting metal coatings 126.

After connection 142 is formed, a resin material is applied on metal wirings 162 exposed at the surface and opened at desired parts by exposure and development and then baked to form a patterned protective film 152. The region where this protective film 152 is formed constitutes protected region 132 of exposed metal wiring 162 to give a flexible wiring board 106 with no metal wiring 162 exposed at undesired parts (FIG. 6(d)).

During patterning protective film 152, metal wiring 162 used for connection to outer circuits remains exposed to form an external terminal 146 as shown in FIG. 6(e).

This flexible wiring board 106 is also formed by assembling a plurality of board pieces 102 a, 102 b, 102 c via low-melting metal coatings 126 and thermoplastic resin films 116, and protected by protective film 152 or non-thermoplastic resin film 112 except for external terminal 146 of metal wiring 162.

Next, a fifth example of flexible wiring board of the present invention is explained.

Referring to FIG. 7(a), references 103 a, 103 b, 103 c represent board pieces used for preparing a fifth example of flexible wiring board (flexible wiring board represented by reference 107 in FIG. 7(c), 7(d)) and having a non-thermoplastic resin film 113. On the top of the non-thermoplastic resin film 113 is formed a patterned metal wiring 163.

Metal wiring 163 consists of a copper thin film 123 and a low-melting metal coating 127 formed on the surface thereof, and has a patterned protective film 153 formed on the surface thereof.

Openings in protective film 153 form exposed regions 137, while metal wiring 163 is not exposed at the surface in protected regions 133 where protective film 153 exists. Exposed regions 137 are used for connecting board pieces 103 a, 103 b, 103 c to each other or to outer circuits as described later.

A thermoplastic resin film 117 is applied on some of exposed regions 137 of one board piece 103 a among these board pieces 103 a, 103 b, 103 c, and then exposed regions 137 of the other two board pieces 103 b, 103 c are opposed to the thermoplastic resin film 117 (FIG. 7(b)).

Then, metal wirings 163 of board pieces 103 a, 103 b, 103 c are brought into contact with each other via thermoplastic resin film 117 and heat and pressure are applied so that thermoplastic resin film 117 first softens to fill the gap between metal wirings 163.

During then, thermoplastic resin film 117 flows out from the gap between two metal wirings 163 pressed against each other and metal wirings 163 come into direct contact with each other. As the temperature of metal wirings 163 rises in this state, low-melting metal coatings 127 melt without scattering, and low-melting metal coatings 127 combine when cooled. Reference 139 represents the resulting single layer low-melting metal coating. Metal wirings 163 are electrically and mechanically connected via the low-melting metal coating 139. Reference 143 represents a connection formed by low-melting metal coating 139 and metal wirings 163.

Board pieces 103 a, 103 b, 103 c are firmly connected via connection 143 and thermoplastic resin film 117 to give a flexible wiring board 107 (FIG. 7(c)).

In exposed regions 137 of board pieces 103 b, 103 c other than connection 143, metal wiring 163 remains exposed to form an external terminal 147 for connecting this flexible wiring board to an outer circuit (FIG. 7(d)).

Next, a sixth example of flexible wiring board of the present invention is explained.

Referring to FIG. 8(a), references 104 a, 104 b, 104 c represent board pieces used for preparing a sixth example of flexible wiring board (flexible wiring board represented by reference 108 in FIG. 8(d), (e)). Each board piece 104 a, 104 b, 104 c has a non-thermoplastic resin film 114 and a patterned metal wiring 164 formed on the non-thermoplastic resin film 114. This metal wiring 164 consists of a copper thin film 124 and a low-melting metal coating 128 formed on the surface thereof.

Each board piece 104 a, 104 b, 104 c has no protective film and metal wiring 164 is exposed at the surface. A thermoplastic resin film 118 is applied on some of exposed regions 138 of one board piece 104 a, and opposed to exposed regions 138 of the other two board pieces 104 b, 104 c (FIG. 8(b)).

Then, metal wirings 164 in the exposed regions 138 are brought into contact with each other and heat and pressure are applied so that thermoplastic resin film 118 softens and then low-melting metal coatings 128 melt without scattering to form a connection 144 at which metal wirings 164 are connected (FIG. 8(c)). Reference 149 in this figure represents a low-melting metal coating formed by combining two low-melting metal coatings 128.

Then, a patterned protective film 154 is formed on the top of exposed copper thin film 164 to give a flexible wiring board 108 with no copper thin film 164 exposed at undesired parts (FIG. 8(d)). The surface of metal wiring 164 is exposed at openings in protective film 154 to form an external terminal 148 used for connection with outer circuits (FIG. 8(e)).

As described above, flexible wiring boards 105-108 of the present invention have high strength because copper thin films 161-164 are protected by non-thermoplastic resin films 111-114 or protective films 151-154 except for regions of external terminals 145-148 and board pieces 101-104 are firmly connected via connections 141-144 and thermoplastic resin films 115-118, and they can be produced with high yields because low-melting metals 125-128 cannot scatter so that no short circuit occurs between metal wirings 161-164.

Although the foregoing description relates to assembling board pieces of the same type 103-106, a board piece 101 a having a metal wiring 161 formed on a thermoplastic resin film 115 as shown in FIG. 5(a) and board pieces 103 b, 103 c having a metal wiring 163 formed on a non-thermoplastic resin film 113 as shown in FIG. 7(a) may also be assembled, for example. In this case, thermoplastic resin film 117 need not be applied on metal wiring 163 if thermoplastic resin film 115 has a large thickness.

Although the foregoing description relates to assembling three board pieces, the present invention is not limited thereto but widely includes flexible wiring boards formed by assembling a plurality of board pieces such as assembling two or four or more elements or layering three or more elements.

Flexible wiring boards 105-108 of the present invention are highly reliable and especially suitable for flexible wiring boards having a relative large area and a complex shape formed by assembling three or more board pieces because they have protective films 151-154 and metal wirings 161-164 are exposed only at regions required to be exposed (such as external terminals 145-148).

Although solders are suitable for the above low-melting metal coating 125, the present invention is not limited thereto but metals and metal alloys having a melting temperature which is higher than the softening temperatures of thermoplastic resin films but not extremely high can be widely used. Low-melting metal coatings 125-128 need not be exposed at the surface, but a gold thin film or the like may be formed for preventing oxidation without any influence on melting and solidifying low-melting metal coatings 125-128 to give a flexible wiring board by assembling board pieces.

Low-melting metal coatings 125-128 need not be formed over the whole region of metal wirings 161-164, but may be formed on at least regions forming connections 141-144.

Low-melting metal coatings 125-128 need not be formed on both of copper thin films 121-124 to be connected to each other, but one of metal wirings 161-164 to be connected to each other may have a low-melting metal coating 125-128.

Flexible wiring boards can also be obtained without necessarily having a low-melting metal coating. When thermoplastic resin films 117, 118 applied on metal wirings 163, 164 have anisotropic conductivity, flexible wiring boards 107, 108 can be obtained only by bonding board pieces 103, 104 under thermal compression without melting and solidifying low-melting metal coatings 127, 128.

As described above, when board pieces of the present invention using a low-melting metal coating are assembled to prepare a flexible wiring board, no melt scatters and no short circuit occurs because thermoplastic resin films soften and fill the gap between metal wirings before the low-melting metal melts.

Thermoplastic resin films used in board pieces and flexible wiring boards of the present invention develop adhesiveness when they soften and return to the original state when they are cooled, whereby non-thermoplastic resin films of board pieces are adhered to each other via the thermoplastic resin films. As a result, the board pieces are assembled via the thermoplastic resin films.

Metal wirings of flexible wiring boards of the present invention should be connected to semiconductor chips or electronic circuits.

Therefore, metal wirings can be partially exposed on flexible wiring boards to serve as external terminals used for connecting flexible wiring boards to outer circuits.

Regions of metal wirings neither located in assembled board pieces nor forming external terminals can be covered with a protective film. Thus, flexible wiring boards have high reliability and durability because metal wirings are protected by non-thermoplastic resin films or protective films.

In this case, two flexible boards can be electrically connected by bonding the flexible boards under thermal compression while metal wirings of the flexible boards are in contact with each other and partially exposed.

When a low-melting metal coating is formed on the metal wiring of at least one of two flexible boards to be assembled and the flexible boards are bonded under thermal compression, the low-melting metal coating melts and then solidify by cooling to form a metallic bond between the metal wiring and the low-melting metal coating, whereby the metal wirings are electrically and mechanically firmly connected via the low-melting metal coating.

However, there is no danger of solder metals or the like scattering when metal wirings are ultrasonically connected and then board pieces are assembled.

When two flexible boards are to be assembled, both flexible boards may have a metal wiring formed on a thermoplastic resin film, but either one flexible board may have a metal wiring formed on a thermoplastic resin film depending on the thickness of the thermoplastic resin film and the area and pitch of the part of the metal wiring used for assembling.

INDUSTRIAL APPLICABILITY

Flexible wiring boards having a complex shape can be obtained by assembling board pieces having a simple shape.

Flexible wiring boards of the present invention are suitable for electronic circuits because of the high reliability and durability. 

What is claimed is:
 1. A board piece comprising: a non-thermoplastic resin film that is made of a plastic resin other than a thermoplastic resin; a thermoplastic resin film formed on the non-thermoplastic resin film; and a metal wiring formed on a surface of the thermoplastic resin film, wherein the metal wiring is partially covered with a resin film, and partially exposed, a low-melting metal coating is formed on the exposed metal wiring, wherein the thermoplastic resin film is adapted to soften under heat to provide a thermoplastic resin for adhesion when the board piece is assembled into a flexible circuit board.
 2. The board piece of claim 1, wherein a solder is used as a material for the low-melting metal coating.
 3. The board piece of claim 1, wherein a gold coating is formed on at least a part of the exposed metal wiring.
 4. The board piece of claim 1, wherein the non-thermoplastic resin consists of a polyimide film.
 5. The board piece of claim 4, wherein the thermoplastic resin film consists of a thermoplastic polyimide film.
 6. A flexible wiring board comprising: at least two board pieces each having a non-thermoplastic resin film that is made of a plastic resin other than a thermoplastic resin, a thermoplastic resin film formed on the non-thermoplastic resin film, and a metal wiring formed on a surface of the thermoplastic resin film, wherein the at least two board pieces are adhered to each other via the thermoplastic resin films by heating the metal wirings of the at least two board pieces in contact with each other, wherein the heating softens plastic resins in the thermoplastic resin films and the softened thermoplastic resins insert themselves between connections of the metal wirings in contact with each other.
 7. The flexible wiring board of claim 6, wherein a low-melting metal coating is formed on a surface of at least one of the metal wirings in contact with each other so that the board pieces are heated to melt the low-melting metal coating, which then solidifies to connect the metal wirings to each other.
 8. The flexible wiring board of claim 6, wherein the metal wirings in contact with each other are connected by ultrasonic wave vibration.
 9. The flexible wiring board of claim 8, wherein a gold coating is formed on at least one of the metal wirings to be connected by ultrasonic wave vibration.
 10. A flexible wiring board formed by assembling at least three board pieces each having a resin film and a metal wiring, wherein the metal wirings of a first and second board pieces among the board pieces are partially connected and fixed to the metal wiring of a third board piece and a thermoplastic resin is filled between the metal wirings in connecting and fixing regions while the metal wirings in other regions are partially covered with a protective film and partially exposed.
 11. The flexible wiring board of claim 10 wherein the resin film of at least one of the board pieces to be assembled has a multilayer structure consisting of a non-that is made of a plastic resin other than a thermoplastic resin, a thermoplastic resin film, and wherein the metal wiring is formed on the thermoplastic resin film.
 12. The flexible wiring board of claim 10 wherein the board pieces are connected to each other by applying a thermoplastic resin film on at least one of the metal wirings, assembling the board pieces, and heating the metal wirings such that a thermoplastic resin constituting the thermoplastic resin film softens and fills between the metal wirings in connecting regions.
 13. The flexible wiring board of claim 10, wherein the metal wirings are fixed to each other with a solder.
 14. The flexible wiring board of claim 10 further comprising an opening in the protective film.
 15. A process for manufacturing a flexible wiring board by assembling a plurality of board pieces each having a resin film and a metal wiring provided on the resin film, wherein the resin film of at least one of the plurality of board pieces to be assembled has a multilayer structure comprising a non-thermoplastic resin films, that is made of a plastic resin other than a thermoplastic resin, and a thermoplastic resin film, wherein the metal wiring is provided on the thermoplastic resin film and the board pieces to be assembled are pressed against each other under heating such that a thermoplastic resin constituting the thermoplastic resin film softens and inserts itself between connections of the metal wirings in contact with each other.
 16. The process of claim 15, wherein the metal wirings of the board pieces are connected torch other by forming a low-melting metal coating on a surface of the metal wiring of at least one of the board pieces to be assembled and pressing the board pieces against each other under heating to melt the low-melting metal coating.
 17. A process for manufacturing a flexible wiring board, comprising: assembling a plurality of board pieces each having a resin film and a metal wiring provided on the resin film, wherein the resin film of at least one of the plurality of board pieces to be assembled has a multilayer structure comprising a non-thermoplastic resin film, that is made of a plastic resin other than a thermoplastic resin, and a thermoplastic resin film, wherein the metal wiring is provided on the thermoplastic resin film; and pressing the plurality of board pieces against each other under heating after applying ultrasonic wave to the board pieces in a superposed state to connect the metal wirings of the board pieces to each other by vibration energy of the ultrasonic wave.
 18. The process of claim 17 wherein a gold coating is formed in advance on a surface of at least one of the metal wirings to be connected.
 19. A process for manufacturing a flexible wiring board, comprising: assembling a plurality of board pieces each having a resin film and a metal wiring provided on the resin film, wherein the resin film of at least one of the plurality of board pieces to be assembled has a multilayer structure comprising a non-thermoplastic resin film, that is made of a plastic resin other than a thermoplastic resin, and a thermoplastic resin film, wherein the metal wiring is provided on the thermoplastic resin film; and pressing the plurality of board pieces in a superposed state against each other under heating while applying ultrasonic wave to connect the metal wirings of the board pieces to each other by vibration energy of the ultrasonic wave.
 20. The process of claim 19 wherein a gold coating is formed in advance on a surface of at least one of the metal wirings to be connected.
 21. A process for manufacturing a flexible wiring board by assembling a plurality of board pieces each having a resin film and a metal wiring provided on the resin film, wherein the metal wirings of the plurality of board pieces are connected to each other by providing a thermoplastic resin film between the metal wirings of the plurality of board pieces and pressing the board pieces against each other under heating to force the metal wirings into the thermoplastic resin film, wherein the metal wirings of the board pieces are connected to each other by forming a low-melting metal coating on a surface of the metal wiring of at least one of the board pieces to be assembled and pressing the board pieces against each other under heating to melt the low-melting metal coating. 